Process for combatting slime in paper pulp by using amidinoureas and amidinothioureas

ABSTRACT

A METHOD OF COMBATTING SLIME IN PAPER PULP WHICH COMPRISES USING ANTIBACTERIAL AND ANTIFUNGAL MONO- AND DISUBSTITUTED AMIDINOUREAS AND AMIDINOTHIOUREAS WHICH ARE OBTAINED BY INTERACTION OF GUANIDINES AND ISOCYANATES OR ISOTHIOCYANATES.

US, Cl, 162 161 14 Claims ABSCT OF THE DISCLOSURE A method of combatting slime in paper pulp which comprises using antibacterial and antifungal monoand disubstituted amidinoureas and amidinothioureas which are obtained by interaction of guanidines and isocyanates or isothiocyanates,

This application is a division of our copending application Ser. No. 749,986, filed Aug. 5, 1968, now Pat. No. 3,652,766, which is a continuation-inpart of our now abandoned application Ser. No. 556,897, filed June 13, 1966, which in turn is a continuation-in-part of our now abandoned application Ser. No. 462,077, filed June 7, 1965.

This invention relates to chemical compounds classified as amidinoureas and amidinothioureas, to the preparation of the same and to a process for combatting microorganisms therewith.

The invention sought to be patented, in its process aspect, is described as residing in the concept of applying to a medium, in order to obviate objectionable or deleterious microorganisms, a composition of matter containing a chemical compound selected either from the group of compounds which, in the form of the free base, has the structural formula r R-NH-(i-NH-C-NH-R Formula. I

wherein X is a member of the group consisting of oxygen and sulfur and one of R and R is alkyl and the other of R and R is a member of the group consisting of hydrogen and alkyl, the total number of carbon atoms in R and R being 8-24; or from the group of compounds which, in the form of the free-base, has the structural f rmula 'Y-NH-C-NH-(iJ-NH-Y' Formula II wherein: X is a member of the group consisting of oxygen and sulfur; one of Y and Y is a member of the group consisting of hydrogen, alkyl containing 1-18 carbon atoms, alkenyl containing 3-18 carbon atoms, alkoxyalkyl containing 3-17 carbon atoms, alkylthioalkyl containing 33-17 carbon atoms, cycloalkyl containing 3-8 carbon atoms, di(lower alkyl)aminoalky1 containing 4-10 can bon atoms, morpholinoalkyl containing 6-10 carbon atoms, and piperidinoalkyl containing 7-11 carbon atoms; and the other of Y and Y is a member of the group consisting of alkenyl containing 3-18 carbon atoms, alkox-yalkyl, containing 3-17 carbon atoms, alkylthioalkyl containing 3-17 carbon atoms, cycloalkyl containing 3-8 carbon atoms, di(lower alkyl)aminoall yl containing 4-10 carbon atoms, morpholinoalkyl containing 6-10 carbon atoms, and piperidinoalkyl containing 7-11 carbon atoms.

The invention sought to be patented, in its composiiterated Sept. 19, NW2

tion aspect, is described as residing in the concept of a chemical compound having the structural formula wherein: X is oxygen or sulfur; Y" and Y' may be the same or different and are members of the group consisting of alkyl containing 1-18 carbon atoms, alkenyl containing 3-18 carbon atoms, alkoxyalkyl containing 31-17 carbon atoms, alkylthioalkyl containing 3-17 carbon atoms, cycloalkyl containing 3-8 carbon atoms, di{lower alkyl) aminoalkyl containing 4-19 carbon atoms, morpholinoalkyl containing 6-1() carbon atoms or piperidinoalkyl containing 7-11 carbon atoms; Y" also is hydrogen when X is oxygen and Y is alkenyl containing 3-18 carbon atoms, alkylthioalkyl containing 3-17 carbon atoms, di(lower a1kyl)aminoalkyl containing 4-10 carbon atoms, morpholinoalkyl containing 6-10 carbon atoms or piperidinoalkyl containing 7-11 carbon atoms; and Y" also is hydrogen when X is sulfur and Y' is alkyl containing 8-18 carbon atoms, alkoxyalkyl containing 3-17 carbon atoms, alkylthioalkyl containing 3-17 carbon atoms, cycloalkyl containing 3-8 carbon atoms, di(lower alkyl) aminoalkyl containing 4-10 carbon atoms, mcrpholino alkyl containing 6-10 carbon atoms or piperidinoalkyl containing 7-11 carbon atoms.

The compounds of Formulas I, II and III are basic substances which interact with one or, in the instances of the morpholinoalkyl and piperidinoalkyl compounds, two or three equivalents of an organic or inorganic acid to form the corresponding acid-addition salts. These acid addition salts and the free bases of course have the common structural entity represented by the structural formulas, Formula I, Formula II, or Formula III, as the case may be. The acid-addition salts are the full equiva lents of the free base forms, and the new compounds of this invention include both the free bases and the acidaddition salts thereof. The novel feature of the compounds of the invention thus resides in the concept of the bases and the acid-addition salts thereof. The novel feature of the compounds of the invention thus resides in the concept of the bases and cationic forms of the new amidinoureas and amidinothioureas and not in any particular acid moiety or acid anion associated with the salt forms of our cone pounds; rather, the acid moieties or anions which can be associated in the salt forms are in themselves neither novel not critical and therefore can be any acid anion or acidlike substance capable of salt formation with bases. It will be appreciated that in aqueous solutions the base form and the acid-addition salt form of the compounds of the invention possess a common protonated cation or ammo=- mum 1011.

Thus, the acid-addition salts discussed above and claimed herein are prepared from any organic acid, incrganic acid (including organic acids having an inorganic group therein), or organometallic acid as exemplified by o ganic monoand polycarboxylic acids such as found, for example, in Beilsteius 'Organische Chemie, 4th ed., V V, X, XIV, XVII, XIX, XXI, XXII, and XXV; organic monoand polysulfonic and -sulfinic acids such as found, for example in Beilstein vols. VI, XI, XVI, and XXII; organic phosphonic and phosphinic acids such as found, for example, in Beilstein vols. XI and XVI; organic acids of arsenic and antimony such as found, for example, in Beilstein vol. XVI; organic heterocyclic car-= boxylic, sulfonic, and sulfinic acids such as found, for example in Beilstein vols. XVIII, XXII, and XXV; acidic ion-exchange resins; and inorganic acids of any acid form ing element or combination of elements such as found in Mellor, Comprehensive Treatise on Inorganic and Theoretical Chemistry, Longmans, Green and Co., New York, N.Y., vols. I-XVI. In addition, other salt-forming compounds which are acidic in their chemical properties but which are not generally considered as acids in the same sense as carboxylic or sulfonic acids are also considered to be among the numerous acids which can be used to prepare acid-addition salts of the compounds of the invention, Thus there are also comprehended acidic phenolic compounds such as found, for example, in vol. VI in Beilstein, acidic compounds having activated or acidic hydrogen atoms, as for example, picrolonic acid, or barbituric acid derivatives having an acidic proton such as found, for example, in Cox et al., Medicinal Chemistry, vol. IV, John Wiley and Sons, Inc., New York, NY. (1959). Also comprehended as salt forming agents are so-called Lewis acids which lack a pair of electrons in the outer electron shell and react with basic compounds having an unshared pair of electrons to form salts, for example boron tri-fluoride.

Representative acids for the formation of the acidaddition salts include formic acid, acetic acid, isobutyric acid, alpha-mercaptopropionic acid, trifluoroacetic acid, malic acid, fumaric acid, succinic acid, succinamic acid, glutamic acid, tartaric acid, oxalic acid, pyromucic acid, citric acid, lactic acid, glycolic acid, gluconic acid, saccharic acid, ascorbic acid, penicillin, benzoic acid, phthalic acid, salicyclic acid, 3,5-dinitrobenzoic acid, anthranilic acid, pamoic acid, cholic acid, Z-pyridinecarboxylic acid, 3-hydroxy-2-naphthoic acid, picric acid, quinic acid, tropic acid, 3-indoleacetic acid, barbituric acid, sulfamic acid, methanesulfonic acid, ethanesulfonic acid, isethionic acid, benzenesulfonic acid, p-toluenesulfonic acid, butylarsonic acid, methanephosphonic acid, acidic resins, hydrofluoric acid, hydrochloric acid, hydrobromic acid, hydriodic acid, perchlcric acid, nitric acid, sulfuric acid, phosphoric acid, hydrocyanic acid, phosphotungstic acid, molybdic acid, arsenic acid, and the like.

The acid-addition salts are prepared in conventional fashion, for instance either by direct mixing of the acid and the base or, when this is not appropriate, by dissolving either or both of the acid and the base separately in a suitable solvent and mixing the two solutions. or by dissolving both the acid and the base together in a solvent. The resulting acid-addition salt is isolated by filtration, if it is insoluble in the reaction medium, or by evaporation of the reaction medium to leave the acid-addition salt as a residue,

Our new bases of Formulas I, II and III and the acidaddition salts thereof have biocidal and biostatic properties and are particularly useful as antibacterial and antifungal agents. Thus, when tested by standard serial dilution procedures, these compounds were found to have bactericidal, hacteriostatic, fungicidal, and fungistatic activity in vitro. Moreover, some of these compounds are effective in the control of phytopathogenic microorganisms, for instance, having useful activity against bacterial and fungal infections in plants, for example late blight (Phytopizrhora infestans) and bacterial spot (Xantomonas vesicatoria) on tomatoes (Lycopersicon esculentum) and bean rust (Uromyces plzaseoli typica) on pinto beans (Pilaseolus vulgaris) The new bases of Formulas 1, I1 and III and the acidadd ition salts thereof are useful as disinfecting and sanitizing agents for application to living and non-living surfaces by conventional swabbing, padding, spraying, immersrng, rinsing, and the like techniques. Depending on the particular purpose involved, the compounds are used in aqueous solution, as in water or in aqueous detergent solutions, or in the form of solutions in organic solvents. I The acid-addition salts of the bases of Formulas I, II and III are useful not only as disinfecting and sanitizing agents, as above-indicated, but are also useful as characterizing or identifying derivatives of the free bases and in isolation or purification procedures. Moreover, the acidaddition salts react with strong bases, such as alkali metal 4 hydroxides, to generate the free bases, and accordingly all of the salts, regardless of considerations of solubility, toxicity, physical form, or the like of a particular species of acid-addition salt, are useful for the purposes of our invention since they are sources of the free bases.

It will be appreciated from the above that if one or more of the characteristics, such as solubility, molecular weight, physical appearance, toxicity, or the like of a given acid-addition salt render it unsuitable for the particular desired purpose, as for example, use as an antibacterial agent or in an isolation or purification procedure, or the like, the acid-addition salt can be converted to the free base and then to another, more suitable acid-addition salt, for instance a pharmaceutically-acceptable salt when a pharmaceutical use is involved.

The l (R) amidino 3 (R')-ureas and the 1-(R)- amidino-3-(R')-thioureas of Formula I and the 1-(Y)- amidino 3 (Y)-ureas and the 1-(Y-amidino)-3- (Y)-thioureas of Formula II, except those species wherein R' and Y are hydrogen, are obtained by interacting a 1-(R)-guanidine or a 1-(Y)-guanidine with approximate 1y one molecular proportion of an isocyanate or isothiocyanate having the structural formula R'NCX Formula IV for the preparation of the Formula I compounds and having the structural formula Y'-NCX Formula V for the preparation of the Formula II compounds, wherein: R is hydrogen or alkyl and R is alkyl, the total number of carbon atoms in R and R being 8-24;

Y is a member 0 fthe group consisting of hydrogen, alkyl containing 1-18 carbon atoms, alkenyl containing 33-18 carbon atoms, alkoxyalkyl containing 3-17 carbon atoms, alkylthioalkyl containing 3-17 carbon atoms, cycloalkyl containing 3-8 carbon atoms, di(lower alkyl)- aminoalkyl containing 4-10 carbon atoms, morpholinoalkyl containing 6-10 carbon atoms, and piperidinoalkyl containing 7-11 carbon atoms; Y is a member of the group consisting of alkenyl containing 3-18 carbon atoms, alkoxyalkyl containing 3-17 carbon atoms, alkylthioalkyl containing 33-17 carbon atoms, cycloalkyl containing 3-8 carbon atoms, di(lower alkyl)aminoalkyl containing 4-10 carbon atoms, morpholinoalkyl containing 6-10 carbon atoms, and iperidinoalkyl containing 7-11 carbon atoms; and X in each instance is a member of the group consisting of oxygen and sulfur, In a convenient method of carrying out this reaction, sodium and dry acetone are mixed together, and then the guanidine in the form of its hydro chloride or sulfate is added, and this is followed by the isocyanate or isothiocyanate reactant; approximately equimolar amounts each of the sodium, the l-(R or Y)- guanidine salt, and the isocyanate or isothiocyanate are used, and the method can be carried out at room temperature.

The 1 (R)-amidino 3 (R')-ureas of Formula '1' wherein R is hydrogen and the 1-(Y)-3-(Y)'ureas of Formula II wherein Y is hydrogen are obtained by hydrolyzing with a strong acid a 1-(R)-3-cyanoguanidine having the structural formula IIIH R-NH-CNI-I*CN Formula VI or a l-(Y)-3-cyanoguanidine having the structural formula NII Y-NII-8-NII-CN Formula VII wherein R is alkyl containing 8-24 carbon atoms and Y is a member of the group consisting of alkenyl containing 3-18 carbon atoms, alkoxyalkyl containing 3-17 carbon atoms, alkylthioalkyl containing 3-17 carbon atoms, cycloalkyl containing 38 carbon atoms, di(lower alkyl) aminoalkyl containing 4-1() carbon atoms, morpholinoalkyl containing 6-10 carbon atoms, and piperidinoalkyl containing 711 carbon atoms. Conveniently, this hydrolysis is carried out by refluxing the l-(R or Y)-3 cyanoguanidlne with concentrated hydrochloric acid.

The 1 (R)-amidino 3 (R)-thioureas of Formula I wherein R is hydrogen and the l-(Y)-amidino-3-(Y')- thioureas of Formula II wherein Y is hydrogen are obtained by interacting one equivalent of a l-(R)-3-cyano guanidine having the structural Formula V or a l-(Y)- B-cyanoguanidine having the structural Formula VI, as hereinabove defined, with two equivalents of hydrogen sulfide. Conveniently the cyanoguanidine is heated with a saturated lower alkanolic solution of hydrogen sulfide at 70-80 C. in a closed vessel. For best results, the reaction mixture is heated for forty-eight hours or longer.

The 1 a ("Y") amidino 3 (Y") ureas and the 1 (Y" u amidino) 3 (Y) thioureas of Formula III are obtained by interacting a 1 (Y") guanidine with approximately one molecular proportion of an isocyanate or isothiocyanate having the structural formula Y-NCX Formula VIII wherein Y", Y', and X have the same respective meanings indicated hereinabove in relation to Formula III. In a convenient method of carrying out this reaction, sodium and dry acetone are mixed together, and then the guanidine in the form of its hydrochloride or sulfate is added, and this is followed by the isocyanate or isothiocyanate reactant; approximately equimolar amounts each of the sodium, the 1 (Y") guanidine salt, and the isocyanate or isothiocyanate are used, and the method can be carried out at room temperature.

The intermediates required for the preparation of our new compounds are all old and well-known classes of compounds and are readily obtained by conventional preparative procedures. Thus, for example, the isocyanates and isothiocyanates of Formulas IV, V and VIII are obtained by interaction of phosgene or thiophosgene with a primary amine having the formula R'NH YNH or Y--NH or the hydrochlorides thereof, wherein R, Y, and Y' have the same significance as indicated hereinabove in connection with Formulas IV, V and VIII. The l (R) 3 cyanoguanidines of Formula VI and the 1 (Y) 3 cyanoguanidines of Formula VII are obtained, for example, by interaction of dicyanamide, or metal salt thereof, with a primary amine having the for mula R-NH or Y-NH or acid-addition salt thereof, wherein R and Y have the same significance indicated hereinabove in connection with Formulas VI and VII, respectively. The 1 (R, Y and Y") guanidines include guanidine itself, which is readily available, and the substituted guanidines which are obtained, for example, by interaction of ammonium chloride with a substituted cyanamide having the formula RNHCN, Y-NHCN or Y-NH-CN, or by interaction of 2-methyl-2 thioseudourea sulfate with a primary amine having the formula R-NHz, Y--NH or Y-NH wherein R, Y and Y have the same significance indicated hereinabove in connection with Formulas VI, VII and VIII, re spectively.

We especially prefer those compounds of this invention in which R and R in Formula I contain a total of 9-16 carbon atoms, Y and Y in Formula II, and Y and Y in Formula III contain a total of 9-l6 carbon atoms since these preferred compounds have particularly high anti-= bacterial and antifungal activities and hence have been found to be particularly useful as antibacterial and antifungal agents.

The chemical structures of the compounds of this invention followed from the modes of preparation from the elementary analyses of the products, and from spectral data on the compounds.

Our invention is illustrated by the following examples without, however, being limited thereto.

EXAMPLE 1 (A) 4.1 g. of sodium was added to 200 ml. of dry acetone and the mixture was refluxed for ten minutes and after the resulting mixture cooled to room temperature there was added in one portion, with strong stirring, 19.1 g. of guanidine hydrochloride. The resulting reaction mixture was stirred for forty-five minutes, and there was added dropwise, at room temperature and over a period of one-half hour, a solution of 23.2 g. of n-octyl isocyanate in 100 ml. of dry acetone. The reaction mixture thus obtained was stirred at room temperature for three hours and then was evaporated under reduced pressure to reduce its volume by half and poured into 250 ml. of cold water. (In following this procedure in the preparation of related species of this invention, it was found in some instances that instead of pouring the reaction product into water it was desirable and in some cases neces-= sary for ready recovery of the product to evaporate the reaction mixture to dryness and then purify the resulting residue.) The mixture was chilled in a refrigerator overnight. The solid precipitate which formed was collected on a filter, washed with cold water, and dried. The dry solid was dissolved in 250 ml. of Warm diethyl ether, and the solution was treated with decolorizing charcoal and filtered. The filtrate was warmed to evaporate off about 100 ml. of ether and cold petroleum ether was added gradually until a slight turbidity was produced. The mix= ture was cooled and the solid which precipitated was collected on a filter and dried in a 'vacuum desiccator. The solid thus obtained, which weighed 28.5 g., was recrystallized from diethyl ether-petroleum ether mixture to yield 24.1 g. of 1 amidino 3 n octylurea, having the structural formula.

as a white crystalline solid which melted at 102-106 C. The solubility of this base in water at 25 C. was less than 0.25 percent. It was soluble in percent ethyl al cohol at 25 C. to the extent of 5 percent (w./v.); a precipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

(B) When an equivalent amount of n-octyl isothio= cyanate is substituted for the n-octyl isocyanate in the procedure described in part (A) above, there is obtained as the product 1-amidino-3-n-octylthiourea, having the structural formula (C) When an equivalent amount of iso-octyl iso cyanate is substituted for the n-octyl isocyanate in the procedure described in part (A) above, there is obtained as the product 1-amidino-3-iso-octylurea, having the struc= tural formula (D) When an equivalent amount of tert-octyl isothiocyanate is substituted for the n-octyl isocyanate in the procedure described in part (A) above, there is obtained as the product l-amidino-B-tert-octylthiotuea, having the structural formula (B) When an equivalent amount of cyclohexyl isocy= anate is substituted for the n-octyl isocyanate in the procedure described in part (A) above, there is obtained as the product l-amidino-3--cyclohexylurea, having the structural formula (F) When an equivalent amount of Z-diethylaminoethyl isocyanate is substituted for the n-octyl isocyanate in the procedure described in part (A) above, there is obtained as the product 1-amidino-3-(Z-diethylaminoethyl)urea, having the structural formula (G) When an. equivalent amount of S-morpholinoamyl isocyanate is substituted for the n-octyl isocyanate in the procedure described in part (A) above, there is obtained as the product l-amidino-3-(5-morpholinoamyl)urea, having the structural formula (H) When an equivalent amount of 3-piperidinopropyl isocyanate is substituted for the n-octyl isocyanate in the procedure described in part (A) above, there is obtained as the product 1-amidino-3-(3-piperidinopropyl)urea, having the structural formula EXAMPLE 2 (A) Proceduring in a manner similar to that described above in Example 1, and using 3.2 g. of sodium, 14.3 g. of guanidine hydrochloride, and 18.3 g. of n-nonyl isocyanate, there was obtained 18.5 g. of l-amidino-3-n-nonylurea, having the structural formula The solubility of this base in Water at 25 C. was less than 0.25 percent. In 95 percent ethyl alcohol at 25 C., it was soluble to the extent of 5 percent (w./v.); a precipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

(B) By treatment of l-amidino-3-n-nonylurea with hydrobromic acid in isopropyl alcohol there was obtained 1-amidino-3-n-nonylurea hydrobromide as a white crys talline solid which melted at 80-82" C. This salt was soluble in water at 25 C. to the extent of 1 percent. The pH of the 1 percent solution was 4.7; when the pH was gradually raised by addition of N/ sodium hydroxide solution, a precipitate formed at pH 6.5.

(C) When an equivalent amount of iso-nonyl isothiocyan-ate is substituted for the n-nonyl isocyanate in the procedure described in part (A) above, there is obtained as the product 1-amidino-3-iso-nonylthiourea, having the as a white crystalline solid which melted at 110l12 C. The solubility of this base in water at C. was less NH (H) than 0.25 percent. In 95 percent ethyl alcohol at 25 C., it was soluble to the extent of 5 percent (w./v.); a pre= cipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

(B) The hydrobromide of the above base was prcpared as follows: 10 g. of 1-amidino-3-n-decylurea was dissolved in ml. of warm methyl alcohol. The resulting solution was cooled to room temperature, and a solution of hydrogen bromide in diethyl ether was added until the pH of the mixture was approximately 6. The ether was evaporated off under reduced pressure, and to the oily residue was added 200 ml. of anhydrous diethyl ether. The mixture was filtered to collect the solid which formed. The solid thus collected, which weighed 12 g, was dissolved in 30 ml. of warm methyl alcohol, 400 ml. of anhydrous diethyl ether was added, and the mixture was cooled. The solid which precipitated from solution was collected on a filter, dried overnight in a vacuum oven at 35 C. There was thus obtained 9.4 g. of l-ami dino-3-n-decylurea hydrobromide as a white crystalline solid which melted at 7882 C. The solubility of this hydrobromide in water at 25 C. was 0.5 percent. The pH of the 0.5 percent aqueous solution was 5.0; when N/ 10 sodium hydroxide solution was gradually added to this solution, a precipitate formed at pH 5.5.

(C) To a solution of 17 g. of 1-amidino-3-n-decylurea in 150 ml. of methyl alcohol there was added 5 percent sulfuric acid until the pH of the mixture was approximately 3. The mixture was cooled, and the solid which precipitated was collected on a filter and recrystallized from ml. of methyl alcohol to yield 18 g. of l-ami dino-3-n-decylurea sulfate which melted at l31-132 C. The solubility of this sulfate in water at 25 C. was less than 0.25 percent; and its solubility in percent ethyl alcohol at 25 C. was less than 1 percent (w./v.).

EXAMPLE 4 Proceeding in a manner similar to that described above in part (A) of Example 1, and using 3.6 g. of sodium, 16.2 g. of guanidine hydrochloride, and 29.8 g. of n-decyl isothiocyanate, there was obtained 16.0 g. of l-amidino- 3-n-decylthiourea, having the structural formula II E I'I2N-- C-NH-C--NII- CH2 CH2) :5-0 H; as a white crystalline solid which melted at 7l-72 C. The solubility of this base in water at 25 C. was less than 0.25 percent. In 95 percent ethyl alcohol, at 25 C. it was soluble to the extent of 5 percent (w./v.); a precipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

EXAMPLE 5 (A) Proceeding in a manner similar to that described above in Example 1, and using 4.3 g. of sodium, 19.1 g. of guanidine hydrochloride, and 29.6 g. of n-undecyl isocyanate, there was obtained 30 g. of 1-amidino-3-n-un decylurea, having the structural formula as a white crystalline solid which melted at l09-l10 C. The solubility of this base in water at 25 C. was less than 0.25 percent. In 95 percent ethyl alcohol at 25 CL, it was soluble to the extent of 5 percent (w./v.); a precipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

(B) By adding to a solution of 10 g. of 1-amidino3- n-undecylurea in 70 ml. of methyl alcohol suificient ethereal solution of hydrogen bromide to give a mixture having pH 5, and isolating and recrystallizing the resultant product from methyl alcohol-diethyl ether mixture, there was obtained 10.5 g. of l-amidino-3-n-undecylurea hydrbromide as a white crystalline solid which melted at 82- 83 C. The solubility of this hydrobromide in water at 25 C. was less than 0.25 percent. It was soluble in 95 percent ethyl alcohol at 25 C. to the extent of 5 percent (w./v.); a precipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

EXAMPLE 6 (A) Proceeding in a manner similar to that described above in Example 1, and using 2.7 g. of sodium, 12.4 g. of guanidine hydrochloride, and 21.1 g. of n-dodecyl isocyanate, there was obtained 23.0 g. of 1-amidino-3-ndo-' decylurea, having the structural formula as a white crystalline solid which melted at 100-103 C. The solubility of this base in water at 25 C. was less than 0.25 percent. Its solubility in 95 percent ethyl alcohol at 25 C. was less than 1 percent (w./v.).

Interaction of this base with hydrogen bromide yielded 1-amidino-3-n-dodecylurea hydrobromide as a white crystalline solid which melted at 87-89 C. The solubility of this hydrobromide in water at 25 C. was less than 0.25 percent. It was soluble in 95 percent ethyl alcohol at 25 to the extent of 1 percent (w./v.); no precipitate formed when the 1 percent alcoholic solution was diluted with four volumes of water, the pH of the thus-diluted solution being 4.1.

EXAMPLE 7 Proceeding in a manner similar to that described above in Example 1, and using 2.7 g. of sodium, 12.4 g. of guanidine hydrochloride, and 22.7 g. of n-dodecyl isothiocyanate, there was obtained 12.8 g. of 1-atnidino-3-n-dodecylthiourea, having the structural formula as a white crystalline solid which melted at 75-80 C. The solubility of this base in water at 25 C. was less than 0.25 percent. In 95 percent ethyl alcohol, at 25 C., it was soluble to the extent of 1 percent (w./v.); a rare cipitate formed when the 1 percent alcoholic solution was diluted with four volumes of water.

EXAMPLE 8 (A) Proceeding in a manner similar to that described above in Example 1, and using 2.7 g. of sodium, 12.4 g. of guanidine hydrochloride, and 23.9 g. of n-tetradecyl isocyanate, there was obtained 20 g. of 1-amidino-3-ntetradecylurea, having the structural formula as a white crystalline solid Which melted at 100-104 C. The solubility of this base in "water at 25 C. was less than 0.25 percent; and its solubility in 95 percent ethyl alcohol at 25 C. was less than 1 percent (w./v.).

(B) Proccediug in a manner similar to that described in Example 1, and using 2.7 g. of sodium, 12.4 g. of guanidine hydrochloride, and 25.6 g. of n-tetradecyl isothiocyanate, there was obtained 13.7 g. of 1-amidino-3-ntetradecylthiourea, having the structural formula as a white crystalline solid which melted at 77-79 C. The solubility of this base in water was less than 0.25 percent. In 95 percent ethyl alcohol at 25 C., it was soluble to the extent of 5 percent (w./v.); a precipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

1 EXAMPLE 9 (A) Proceeding in a manner similar to that described above in Example 1, and using 3.4 g. of sodium, 15.3 g. of guanidine hydrochloride, and 30.1 g. of n-hexadecyl isocyanate, there was obtained 23.7 g. of 1=amidino-3-n-= hexadecylurea, having the structural formula 0 H N( -NH-( i--NH-CHz(CH2)i4-CH3 as a white crystalline solid which melted at 107-109" C. The solubility of this base in water at 25 C. was less than 0.25 percent. Its solubility in percent ethyl alcohol at 25 C. was less than 1 percent (w./v.).

(B) When an equivalent amount of n-hex'adecyl iso thiosyanate is substituted for the n-hexadecyl isocyanate in the procedure described in part (A) above, there is obtained as the product l-amidino-3-n-hexadecylthiourea, having the structural formula (A) Proceeding in a manner similar to that described above in Example 1, and using 3.2 g. of sodium, 14.3 g. of guanidine hydrochloride, and 18.1 g. of 9-decenyl iso cyanate, there was obtained 16 g. of lamidino-3-(9-decenyl)urea, having the structural formula 15m 0 IIzN-0--NH-- -NH-CHi-(CH2)7-CH: CH as a white crystalline solid which melted at 94-97 C. The solubility of this base in water at 25 C. was less than 0.25 percent. In 95 percent ethyl alcohol at 25 C., it was soluble to the extent of 5 percent (w./v.); a precipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

(B) When an equivalent amount of .Q-decenyl isothio cyanate is substituted for the 9-decenyl isocyanate in the procedure described in part (A) above, there is obtained as the product l amidino-3-(9-decenyl)thiourea, having the structural formula (C) When an equivalent amount of 9-octadecenyl isocyanate is substituted for the Q-decenyl isocyariate in the procedure described in part (A) above, there is obtained as the product 1-amidino-3-(9-octadecenyl)urea, having the structural formula (D) When an equivalent amount of 9 octadecenyl iso thiocyanate is substituted for the 9 decenyl isocyanate in the procedure described in part (A) above, there is Oh" tained as the product il amidino3-(9octadecenyl)thin urea, having the structural formula (A) Proceeding in a manner similar to that described above in Example 1, and using 2.72 g. of sodium, 12.2 5. of guanidine hydrochloride, and 18.0 g. of 3(n-octyloxy)propyl isocyanate, there was obtained 4.0 g. of lamidino-3-[3-(n-octyloxy)propyl]urea, having the struc tural formula is an off-White powder which melted at 74-76 C. This base was soluble in a dilute acidic solution (prepared by mixing 0.36 ml. of N/2 hydrochloric acid and 0.14 ml. of water) at 25 C. to the extent of 10 percent. The pH of a 1 percent solution in the dilute acid was 2.2; no precipitate formed when the pH of this solution was adjusted to 7.0 by addition of N/lO sodium hydroxide solution.

(B) When an equivalent amount of 3-(n-octyloxy) propyl isothiocyanate is substituted for the 3-(n-octyloxy)propyl isocyanate in the procedure described in part (A) above, there is obtained as the product l-amidino- 3-[3-(n--uctyloxy)propyl]thiourea, having the structural formula (C) When an equivalent amount of 6-methoxyhexyl isocyanate is substituted for the 3-(n-octyloxy)propyl isocyanate in the procedure described in part (A) above, there is obtained as the product 1-amidino-3-(6-methoxyhexyl)urea, having the structural formula (D) When an equivalent amount of 8-(n-propyloxy) octyl isothiocyanate is substituted for the 3-(n-octyloxy) propyl. isocyanate in the procedure described in part (A) above, there is obtained as the product l-amidino-3-[8- (n-propyloxy)octyllthiourea, having the structural forrnula (A) Proceeding in a manner similar to that described above in Example 1, and using 2.4 g. of sodium, 11.2 g. of guanidine hydrochloride, and 18.0 g. of S-(n-decyloxy)propyl isocyanate, there was obtained 11 g. of 1- amidino3-[3-(n-decyloxy)propyl]urea, having the structural formula HlN-( ;NH-- NHCHaCIIrCHi O-CHz(CII2) -CH; as a cream colored powder which melted at 78-82 C. The solubility of this base in Water at 25 C. was less than 0.25 percent. In 95 percent ethyl alcohol at 25 C., it was soluble to the extent of percent (w./v.); a pre-= cipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

(B) When an equivalent amount of 3-(n-decyloxy) propyl isothiocyanate is substituted for the 3-(n-decyl-- oxy)propyl isocyanate in the procedure described in part A above, there is obtained as the product I-amidino-S [3--(n-decyloxy)propyl]thiourea, having the structural formula heptyl isocyanate is substituted for the 3-(n-decyloxy) propyl isocyanate in the procedure described in part (A) above, there is obtained as the product 1-amidin0-3-[7- (trdecyloxy)heptyl]urea, having the structural formula (A) Proceeding in a manner similar to that described above in Example 1, and using 2.5 g. of sodium, 11.1 g. of guanidine hydrochloride, and 20 g. of 3-(n-decylthio) propyl isocyanate, there was obtained 18.8 g. of l-amidino-3[3-(n-decylthio)propyl]urea, having the structural formula H1N--O-NH-!L NH-OH:CH:GHz-S-CIIi-(CH2)s-OH as a white solid which melted at 89-92 C. The solubility of this base in water at 25 C. was less than 0.25 percent. In 95 percent ethyl alcohol at 25 C., it was 112 soluble to the extent of 5 percent (w./v.); a precipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

(B) When an equivalent amount of 3-(n-decylthio) propyl isothiocyanate is substituted for the 3-(n-decylthio)propyl isocyanate in the procedure described in part (A) above, there is obtained as the product I-amidino- 3-[3-(n-decylthio)propyl]thiourea, having the structural formula (C) When an equivalent amount of 4-(npropylthio) butyl isocyanate is substituted for the 3-(n-decylthio)propyl isocyanate in the procedure described in part (A) above, there is obtained as the product 1-amidino-3-[4-(m propylthio)butyl]urea, having the structural formula (A) A mixture of 22.4 g. of l-n-decyl-3-cyanoguan-= idine, 78 ml. of isopropyl alcohol, and 16 ml. of concen= trated hydrochloric acid was refluxed for thirty minutes, after which another 6 m1. of concentrated hydrochloric acid was added, and the mixture was refluxed for two hours. The reaction mixture was cooled and was then evaporated under reduced pressure until the mixture began to foam. There was then added 400 ml. of warm water, and the resulting solution was filtered warm through diatomaceous earth repeatedly until a clear filtrate was obtained. The filtrate, which contained 1-(n-decylamidino)urea hydrochloride dissolved therein, was cooled, and the pH was adjusted to approximately 6 by addition of N sodium hydroxide solution, thereby to neutralize the hydrochloride and generate the free base, l-(n-decylamidino)urea, haw ing the structural formula and then a solution of 20 g. of sodium nitrate in 40 ml. of water was added with vigorous stirring. The mixture was chilled for several hours, and the solid which precipitated was collected on a filter and washed with dilute nitric acid and water. The solid was dried under reduced pressure at room temperature (about 25 C.) for four hours and at 30 C. for three hours. This product, which weighed 36 g., was recrystallized from 400 ml. of acetonitrile and then from 70 ml. of isopropyl alcohol to yield 12.0 g. of l-(n--decylamidino)urea nitrate, as a white crystalline solid which melted at 125427 C. The solubility of this nitrate in water was less than 0.25 percent, and in percent ethyl alcohol its solubility was less than 1 percent (W./v.).

(B) When an equivalent amount of lm-octyl-S-cyanm guanidine is substituted for the l-n-decyl-3-cyanoguanidine in the procedure described in part (A) above, there are obtained as the products 1-(n-octy1amidino)urea, having the structural formulav and the nitrate salt thereof.

(C) When an equivalent amount of l-(9-decenyl)-3= cyanoguanidine is substituted for the l-n-decyl 3-cyanoguanidine in the procedure described in part (A) above, there are obtained as the products 1-(9-decenylamidino) urea, having the structural formula t" i CHg=OII--(On2)7"'CII2 'NHC-NI ""CNHQ and the nitrate salt thereof.

(D) When an equivalent amount of 1-[3-(iso-decyb oxy)propyl]-3-cyanoguanidine is substituted for the 1-ndecyl-B-cyanoguanidine in the procedure described in part and the nitrate salt thereof.

(F) When an equivalent amount of 1-cyclooctyl-3-cyanoguanidine is substituted for the 1-n-decyl-3-cyanoguanidine in the procedure described in part (A) above, there are obtained as the products 1-(cyclooctylamidino)urea, having the structural formula CHa-C 2 and the nitrate salt thereof.

.(G) When an equivalent amount of 1-(2-rnorpholino ethyl)-3-cyanoguanidine is substituted for the l-n-decyl- 3--cyanoguanidine in the procedure described in part (A) above, there are obtained as the products 1-[(2-morpholinoethyl)amidino]urea, having the structural formula and the nitrate salt thereof.

(H) When an equivalent amount of 1-(6-piperidino hexyl)-3-cyanoguanidine is substituted for the 1-ndecyl- S-cyanoguanidine in the procedure described in part (A) above, there are obtained as the products 1-[(6-piperidinohexyDamindinoJurea, having the structural formula and the nitrate salt thereof.

EXAMPLE Proceeding in a manner similar to that described above in Example 14, and using 25.2 g. of l-n'dodecyld-cyano guanidine, 68 ml. of isopropyl alcohol, and 16 ml. of concentrated hydrochloric acid, there were obtained i .(n-dodecylamidino)urea hydrochloride, the free base i (mdodecylamidinowrea having the structural formula and 1-(n-dodecylamidino)urea nitrate. The nitrate was a white crystalline solid which melted at l09-1l0 C. The solubility of the nitrate in water at 25 C. was less than 0.25 percent, and in 95 percent ethyl alcohol its solubility was less than 1 percent.

EXAMPLE 16 Proceeding in a manner similar to that described above in Example 14, and using 20 g. of l-n-tetradecyl-S-cyauoguanidine, 70 ml. of isopropyl alcohol, and 9 ml. of hydrochloric acid, there was obtained l-(n-tetradecylamidino)-= urea hydrochloride, the free base l-(n-tetradecylamidino) urea having the structural formula NH 0 GHQ--(CH2 12-CH2-NH--NH-PJ-NH2 and l-(n-tetradecylamidino)urea nitrate. The nitrate (11 g. yield) was dissolved in methyl alcohol and sodium hydroxide solution was added to regenerate the free base, 1-n-tetradecyl-3-cyanoguanidine, which was dissolved in methyl alcohol and treated with ethereal hydrogen bromide solution to yield 5.2 g. of 1-n-tetradecyl-3-cyanoguanidine hydrobromide as a white crystalline solid which melted at 116-1 18 C. The solubility of the hydrobromide in water at 25 C. was less than 0.25 percent. In percent ethyl alcohol at 25 C., the hydrobromide was soluble to the extent of 5 percent ,(w./v.); a precipitate formed slowly when the 5 percent alcoholic solution was diluted with four volumes of water.

EXAMPLE 17 (A) A mixture of 70 g. of 1-n-octy1-B-cyanoguanidine and 800 ml. of a saturated (at 0 C.) solution of hydrogen sulfide in methyl alcohol is heated at 70-80 C. in a closed vessel for forty-eight hours. The reaction mixture thus obtained is evaporated to dryness under reduced pressure leaving a residue consisting of crude 1-(n-octylamidino)thiourea, having the' structural formula i r OHa-(CH|)r-OHa--NH-C-NH-Ci-Nlin Recrystallization of this product yields the pure base.

(B) When an equivalent amount of 1-n-heptadecyl-3-= cyanoguanidine is substituted for the 1-n-octyl-3-cyanoguanidine in the procedure described in part (A) above, there is obtained as the product l-(n-heptadecylamidino) thiourea having the structural formula i i OHP-(CHMW-GHWNHWAMNHMCWNIU (C) When an equivalent amount of 1-[6-(n-hexyh oxy)-hexyl]-3-cyanoguanidine is substituted for the 1-n= octyl-S-cyanoguanidine in the procedure described in part: (A) above, there is obtained as the product 1-[6-(n-hexyloxy)hexylarnidiuo]thiourea, having the structural for mula Nu: s

When an equivalent amount of i-[6-(n-nonyl thio)hexyl]-3'cyanoguanidine is substituted for the i noctyl-3-cyanoguanidine in the procedure described in part (A) above, there is obtained as the product 1-[6-(nnonylthio)hexylamidino]thiourea, having the structural formula (B) When an equivalent amount of 1(7=tctradecenyl)- .3-cyanoguanidine is substituted for the l-n-octyl-B-cyanm guanidine in the procedure described in part (A) above. there is obtained as the product 1 (7 tetradecenyl) amidinothiourea, having the structural formula (A) To a solution obtained by dissolving 4.6 g. of sodium in 300 ml. of dry acetone there was added 32.8 g. of n-butylguanidine sulfate and the resulting mixture was stirred for one hour at room temperature. There was then added dropwise, over a period of one hour, a solution of 19.8 g. of n-butyl isocyanate in 200 ml. of dry acetone, and the mixture thus obtained was stirred overnight at room temperature. (In some instances it was found pref: erable to use an equivalent amount of tert-butyl alcohol instead of acetone both in the reaction with sodium and an equivalent amount of cyclohexyl isocyanate is sub= as the reaction solvent.) The reaction mixture was evapostituted for the n-butyl isocyanate, the product obtained rated under reduced pressure to reduce its volume by half, is l-(4-morpholinobutylamidino)-3-cyclohexylurea, hav= after which it was poured into 250 ml. of cold water. (In ing the structural formula CH2-C 2 CHr-CH: the preparation of related species of this invention by (E) Using the procedure described in part (A), when this procedure, it was found in some instances that instead an equivalent amount of lZ-ethoxydodecylguanidine sulof pouring the reaction product into water it was desirable fate is substituted for the n-butylguanidine and an equiv" and in some cases necessary for ready recovery of the alent amount of 4-(n-octylthio)butyl isocyanate is subproduct to evaporate the reaction mixture to dryness and stituted for the n-butyl isocyanate, the product obtained then purify the resultin residue.) The red oil which is 1 (12 ethoxydodecylamidino)-3-[4 (n-octylthio)- separated from solution was washed twice with water and 15 butyl]urea, having the structural formula I ll CrH5O-CHz--(CH1)10-0Hr-NH-E-NHCNH-CHz-(CH2)2CH2-S-CH2(CH2)0CH:

was then dissolved in diethyl ether. The ethereal solu- EXAMPLE 19 was dned Over anhydrous Calclum .Su1fate.and the Proceeding in a manner similar to that described above ether was then evaporated from the solution to yield l-nin Part (A) of Example 18, and using 4.5 g of Sodium butylamidino-3-n-butylurea, having the structural formula 355 of n amy1guanidine Sulfate and 226 of mamyl N o r isocyanate, there was obtained 14.2 g. of 1-n-arnyl= g g amidino-3-n-amylurea having the structural formula as an oil. This base was dissolved in anhydrous diethyl NH O ether and was converted to its sulfate by addition of a t 1 5 percent ethereal sulfuric acid solution. The resulting CH3-(CH)PCHQTNHTAITNHTIJTNHTCHPWH)"Cm Solution was evaporated, under P P w and the as a white crystalline solid which melted at 8.9-91 C. pasty residue thus obtained was dissolved in 200 ml. of The solubility of this base in water at 250 CD was less methyl alcohol. The methanolic solution was treated with than 0.25 percent In 95 percent ethyl alcohol at Co decolorizing charcoal and after removal of the charcoal it was soluble to the extent f 5 percent (WW/Va); a pm 1116 Solution Was evaporated under reduced pressure- The cipitate formed when the 5 percent alcoholic solution was residue was dissolved in 200 ml. of isopropyl alcohol and 5 diluted i h f volumes f water the solution was evaporated under reduced pressure. The

sticky residue was dissolved in 200 ml. of methyl alcohol EXAMPLE 20 and the methanolic solution was saturated with gaseous Proceeding in a manner similar to that described above ammonia. The mixture was filtered to remove ammonium in part (A) of Example 18, and using 4.5 g. of sodium, sulfate and the filtrate was evaporated under reduced 38.4 g. of n-hexylguanidine sulfate, and 19.8 g. of n-butyl pressure to yield a red oil. This oil was dissolved in 100 isocyanate, there was obtained 21 g. of 1-n-hexylamidino= ml. of anhydrous diethyl ether, 75 ml. of petroleum 3-n-butylurea having the structural formula ether was added, and the resulting solid precipitate was collected on a filter and dried under reduced pressure for 11111 0 four hours at 40 C. This product, which weighed 21.7 CHr-(CHZ)t-"oHr-NIP-JJ NII---NII-CHT-(GHQ LPCH3 g., was recrystallized from benzene (100 ml.)-petroleum ether (30 1 and then from 700 m], f anhydrous as an off-white crystalline powder which melted at 96- ethyl Ethan The, was thus Obtained 103 f 99 C. The solubility of this base in water at 25 C. Was amidino-3-n-butylurea as a white crystalline solid which lessfhan 035 Percent In 95 Pfircfint 6thyl alcohfil at melted at 82--94 C. From the ethereal mother liquor was Solublfi to the extent of 5 Percent it there was recovered 3.1 g. of the same product. The soluprecipitate formed when the 5 Percent alcohoml 501mm" bility of this base in water was less than 0.5 percent. It was diluted Wlth foul" Volumes of Wat? was soluble in 95 percent ethyl alcohol to the extent of EXAMPLE 21 5 percent (w./v.); on addition of four volumes of water to the 5 percent alcoholic solution, the diluted solution, which had a pH of 8.9, remained clear.

(B) When an equivalent amount of n-hutyl isothiocyanatc is used in place of the n-butyl isocyanate in the procedure described in part (A) above, the product obtained is l-n-butylamidino-3-n-butylthiourea, having the 50 structural formula Proceeding in a manner similar to that described above in part (A) of Example 18, and using 3.44 g. of sodium. 28.8 g. of n-hexylguanidine sulfate, and 17.0 g. of n amyl isocyanate, there was obtained 20.0 g. of l-n-hexylarni dino-3-n-amylurea having the structural formula s CHMCHQFCmWNHMgQNHW W as a white crystalline solid which melted at 74-75 C.

(C) when an equivalent amount of 9 decen 1 38C 6 The solubility of this base in water at 25 C. was less nate is used in place of the n-butyl isocyana t e in i he i percent In 95 percent ethyl alcohol at 25 procedure described in part (A) above, the product ob- W Soluble to the extent of 5 Percent prep mined is l nfibutylamidino 3 (9 deceny1)urea, having the c pitate formed when the 5 percent alcoholic solution was Structural formula diluted with four volumes of Water.

Zt|-|IH EXAMPLE 22 Q f (A) Proceeding in a manner similar to that described (D) Using the procedure described above 1n part (A), above in part (A) of Example 18, and using 4.5 g. of when an equivalent amount of 4-morpholinobutylguanisodium, 38.4 g. of n-hexylguanidine sulfate, and 25.4 g.

dine sulfate is substituted for the n-butylguanidine and 75 of n-hexyl isocyanate, there was obtained 11.1 g. of l-nas a white crystalline solid which melted at 75-78 C. The solubility of this base in water at 25 C. was less than 0.25 percent. In 95 percent ethyl alcohol at 25 C. it was soluble to the extent of percent (w./v.); a precipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

(B) By treatment of 6 g. of l-n-hexylamidino-3-n= hexylurea with hydrogen chloride in methanolic solution there was obtained 6.3 g. of l-n-hexylamidino-3-n-hexylurea hydrochloride as a white crystalline solid which melted at 60-62 C. The solubility of this hydrochloride in water at 25 C. was less than 0.25 percent. It was soluble in 95 percent ethyl alcohol at 25 C. to the extent of 5 percent (w./-v.); a precipitate formed slowly when the 5 percent alcoholic soultion was diluted with four volumes of water, the pH of the thus-diluted solution being 4.4.

(C) By treatment of 6 g. of l-n-hexylamidino-B-nhexylurea in methanolic solution with an ethereal solution of hydrogen bromide there was obtained 6.5 g. of l--n-hexylamidino-3-n-hexylurea hydrobromide as a white crystalline solid which melted at 56-60 C. The solubility of this hydrobromide in water at 25 C. was less than 0.25 percent. It was soluble in 95 percent ethyl alcohol at 25 C. to the extent of 5 percent (w./v.); a precipitate formed slowly when the 5 percent alcoholic solution was diluted with four volumes of water, the pH of the thusdiluted solution being 4.3.

(D) By treatment of 6 g. of l-n-hexylamidino-S-nhexylurea with 85 percent phosphoric acid in methanolic solution there was obtained 6.2 g. of 1-n-hexylamidino-3- n-hexylurea phosphate as a white crystalline solid which melted at l06-109 C. The solubility of this phosphate in water at 25 C. was less than 0.25 percent. It was soluble in 95 percent ethyl alcohol at 25 C. to the extent of 5 percent (w./v.); a precipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

(B) By treatment of 6 g. of l-n-hexylamidino-S-m hexylurea with 70 percent glycolic acid in methanolic solution there was obtained 5.5 g. of l-n-hexylamidino- 3-n-hexylurea glycolate as a white crystalline solid which melted at 9498 C. The solubility of this glycolate in water at 25 C. was less than 0.25 percent. It was soluble in 95 percent ethyl alcohol at 25 C. to the extent of 5 percent (w./v.); a precipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

(F) By treatment of 6. g. or l-n-hexylamidino-3-nhexylurea with 85 percent lactic acid in methanolic solu tion there was obtained 5 g. of l-nhexylamidinod n hexylurea lactate as a white crystalline solid which melted at 65-69 C. The solubility of this lactate in a dilute acidic solution (prepared by mixing 0.28 ml. of N/Z hydrochloric acid solution with 19.72 ml. of water) at 25 C. was less than 0.25 percent. It was soluble in 95 percent ethyl alcohol at 25 C. to the extent of 5 percent (w./v.); a precipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

EXAMPLE 23 Proceeding in a manner similar to that described above in part (A) of Example 18, and using 3.44 g. of sodium, 30.9 g. of n-heptylguanidine sulfate, and 19.1 g. of nhexyl isocyanate, there was obtained 26.2 g. of l-nheptylamidino-3-n-hexylurea having the structural formula as a white crystalline solid which melted at 68-72" C. The solubility of this base in a dilute acidic. solution (prepared by mixing 0.36 ml. of N/2 hydrochloric acid and 9.64 ml. of water) at 25 C. was less than 0.25 percent. In percent ethyl alcohol at 25 C. it was soluble to the extent of 5 percent (w./v.); a precipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

EXAMPLE 24 Proceeding in a manner similar to that described above in part (A) of Example 18, 2.7 g. of sodium was dis-= solved in 250 ml. of dry acetone, 25 g. of n-heptyl=- guanidine sulfate was added to the solution, the mixture was stirred for fifteen hours at room temperature; and then a solution of 16.9 g. of n-heptyl isocyanate in 200 ml. of acetone was added dropwise, and the reaction mix= ture was stirred for three hours at room temperature. The reaction mixture was evaporated to half-volume under reduced pressure and the mixture was stored in a refrig erator for two weeks. The solid which had precipitated was collected on a filter, was washed with water and a few ml. of acetonitrile, and dried overnight in a desicca= tor. The yellowish product thus obtained, which weighed 32.2 g., was mixed with 30 ml. of cold acetonitrile, and the solid was collected on a filter, dried overnight in a desiccator, and then recrystallized from acetonitrile to yield 23 g. of 1-n-heptylamidino-3-heptylurea having the structural formula NH 0 CHa-(CHsh-CHr-NH-PJ-NH- --NH-CHr(CH2)r-CHs as a white crystalline solid which melted at 5659 C. This base in methanolic solution was treated with ethereal hydrogen chloride solution to yield 21.3 g. of l-n-heptylamidino-B-n-heptylurea hydrochloride as a white crystalline solid which melted at 71-75 C. The solubility of this hydrochloride in dilute aqueous alkali (prepared by mixing 0.30 ml. of N/2 sodium hydroxide solution with 19.70 ml. of water) at 25 C. was less than 0.25 percent. In 95 percent ethyl alcohol at 25 C. this salt was soluble to the extent of 5 percent (w./v.); a precipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

EXAMPLE 25 (A) 3.68 g. of sodium and 1050 ml. of dry t butyl alcohol were heated together under reflux with vigorous stirring for about two hours. The liquid was cooled to approximately 28 C. and then 25 g. of (3-morpholino= propyl)=guanidine sulfate was added in one portion. After stirring the mixture for thirty minutes, a solution of 9.8.5 g. of n octyl isocyanate in ml. of t-butyl alcohol was added dropwise over a period of twenty minutes. The re= suiting reaction mixture was stirred for two and one halii hours and allowed to stand overnight. The mixture was concentrated on a water bath at 35 45 (,3. The residue was mixed with 250 ml. of acetonitrile and allowed to stand overnight. The mixture was filtered to remove 16.2 g. of solid, and the acetonitrile was distilled from the tiltrate to yield 2.3 g. of a light brown syrup consisting of crude 1-[ (3 morpholinopropyl)-amidino]financtylurea. having the structural formula Approximately 18 g. of this syrup was mixed with 500 ml. of anhydrous diethyl ether, the mixture was filtered through diatomaceous earth, the filtrate was acidified by addition of 22 ml. of 4.3 N alcoholic hydrogen chloride solution, and the mixture was chilled overnight. The solid which had precipitated was then collected on a filter. This solid, which weighed 17.7 g., was recrystallized from iso propyl alcohol, with charcoaling to yield 12.8 g. of solid which was then recrystallized again from isopropyl alco- 1101. There was thus obtained 9.5 g. of 1-[(3-morpholinopropyl)amidino] 3-n-octylurea dihydrochloride as a white powder which melted at l41-143 C. (dec.). This salt was soluble in water at 25 C. to the extent of 20 percent. The pH of the 1 percent aqueous solution was 4.0; when the pH of this solution was gradually raised by addition of N/ 10 sodium hydroxide solution, no precipitate formed at pH 7.

(B) When an equivalent amount of (2-piperidinoethyl)-guanidine sulfate is used instead of (3-morpholinopropyl)-guanidine sulfate in the procedure described in part (A) above, the products obtained are 1-[(2-piperidinoethyl)amidino]-3-n-octylurea, having the structural formula and the dihydrochloride thereof.

(C) Following the procedure described in part (A) above but using an equivalent amount of 4-piperidinobutyl isocyanate in place of n-octyl isocyanate, there are obtained as the products 1-[( 3-morpholinopropyl)amidino]- 3-(4-piperidinobutyl)-urea, having the structural formula 20 thiocyanate, there was obtained 1-amidino-3-n-nonylthio= urea, having the structural formula N i HZN( ;NHC-NH-OHZ(Grim-CH3 as a red oil.

(B) By treatment of I-amidino-3-n-nonylthiourea with ethereal hydrogen chloride there was obtained 1-amidino 3-n-nonylthiourea hydrochloride as a white crystalline solid which melted at 79-81 C. The solubility of this salt in water at C. was less than 0.25 percent; and its solubility in 95 percent ethyl alcohol at 25 C. was less than 1 percent (w./v.).

EXAMPLE 29' Proceeding in a manner similar to that described above in Example 1, and using 2.5 g. of sodium, 10.4 g. of guanidine hydrochloride, and 24.5 g. of n-undecyl isothiocyanate, there was obtained 15.9 g. of 1--amidino-3-nundecylthiourea, having the structural formula The solubility of this base in a dilute acidic solution (0.40 ml. of N/2 hydrochloric acid plus 19.60 ml. of water) and the trihydrochloride thereof.

EXAMPLE 26 Proceeding in a manner similar to that described above in part (A) of Example 25, and using 3.68 g. of sodium, 25 g. of (3morpholinopropyl)guanidine sulfate, and 11.6 g. of n-decyl isocyanate, there were obtained 1-[(3-rnorpholinopropyl)amidino]-3-n-decylurea having the structural formula and the dihydrochloride thereof. The dihydrochloride was obtained as a white powder which weighed 15.2 g. and which melted at 134-135 C. This salt was soluble in water at 25 C. to the extent of 20 percent; the pH of the 1 percent aqueous solution was 4.6, and when the pH was gradually raised by addition of N/ 10 sodium hydrox ide solution no precipitate formed at pH 7.

EXAMPLE 27 Proceeding in a manner similar to that described above in Example 18(A), and using 2.3 g. of sodium, 22 g. of n-octylguanidine sulfate, and 15.5 g. of n-octyl isocyanate, there was obtained 26 g. of 1n-octylamidino-3-n-octylurea having the structural formula as a white crystalline solid which melted at 6062 C. "T he solubility of this base in water at 25 C. was less than 0.25 percent. In 95 percent ethyl alcohol it was soluble to the extent of 5 percent; a precipitate formed when the 5 percent ethanolic solution was diluted with four volumes of water.

EXAMPLE 28 (A) Proceeding in a mannersimilar to that described above in Example 1, and using 3.4 g. of sodium, 14.3 g. of guarudine hydrochloride, and 27.7 g. of n-nonyl isowas less than 0.25 percent. In percent ethyl alcohol at 25 C., it was soluble to the extent of less than 1 per cent (w./v.)

EXAMPLE 30 Proceeding in a manner similar to that described above in Example 1, and using 2.9 g. of sodium, 12.9 g. of guanidine hydrochloride, and 17.9 g. of 3-(n-heptyloxy) propyl isocyanate, there was obtained 1-amidino-3-[3 (nheptyloxy)propyl]urea, having the structural formula as a white powder which melted at 72-74" C. This base was soluble in a dilute acidic solution (0.39 ml. of N/Z hydrochloric acid plus 0.61 ml. of water) at 25 C. to the extent of 5 percent. In 95 percent ethyl alcohol at. 25 C., it was soluble t0 the extent of 5 percent (w./v.); a precipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

EXAMPLE 31 Proceeding in a manner similar to that described above in Example 1, and using 2.6 g. of sodium, 11.2 g. of guanidine hydrochloride, and 18.0 g. of 3-(n-nony1 0Xy)propyl isocyanate, there was obtained 1-amidino- 3 [3-(n-nonyloxy)propyl]urea having the structural formula EXAMPLE 32 (A) Proceeding in a manner similar to that described above in Example 1, and using 2.8 g. of sodium, 12.0 g. of guanidine hydrochloride, and 32.0 g. of 3-(n-undccyloxy)propyl isocyanate, there was obtained 15.7 g. of 1-amidino-3-[3-(n-undecyloxy)propyl]urea, having the structural formula as a white powder which melted at 72-78 C.

(B) Interaction of this base with hydrogen chloride yielded lv-amidino-3-[3-(n undecyloxy)propyl]urea hydrochloride as a white powder which melted at 66-69 C. This hydrochloride was soluble in water at 25 C. to the extent of 20 percent. The pH of a 1 percent aqueous solution was 3.7; when N/ 10 sodium hydroxide solution was gradually added to this solution, a precipitate formed at pH 5.5.

EXAMPLE 33 (A) Proceeding in a manner similar to that described above in Example 1, and using 3.0 g. of sodium, 13.0 g. of guanidine hydrochloride, and 36.6 g. of 3-(n-dodecyloxy)propyl isocyanate, there was obtained 1- amidino-S-[S-(n dodecyloxy)propyl]urea, having the structural formula EXAMPLE 34 Proceeding in a manner similar to that described above in Example 1, and using 2.3 g. of sodium, 9.5 g. of guanidine hydrochloride, and 20.0 g. of S-(n-hexylthio) propyl isocyanate, there was obtained l-arnidino-3[3 (whexylthio)propylJurea, having the structural formula as a white crystalline solid which melted at 71 73 C. The solubility of this base in a dilute acidic solution (0.78 ml. of N/2 hydrochloric acid plus 19.72 ml. oi water) at 25 C. was less than 0.25 percent. In 95 percent ethyl alcohol at 25 (3., it was soluble to the extent of 5 percent (w./v.); a precipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

EXAMPLE 35 Proceeding in a manner similar to that described above in Example 1, and using 1.06 g. of sodium, 4.45 g. of guanidine hydrochloride, and 10.0 g. of B-(n-heptylthio) propyl isocyanate, there was obtained 1-amidino-3-[3- (n-heptylthio)propyl]urea having the structural formula as a white crystalline solid which melted at 79-82 C. The solubility of this base in a dilute acidic solution 22 (0.40 ml. of N/2 hydrochloric acid plus 19.60 ml. of water) at 25 C. was less than 0.25 percent. In per= cent ethyl alcohol at 25 C., it was soluble to the extent of 5 percent (w./v.); a precipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

EXAMPLE 36 Proceeding in a manner similar to that described above in Example 1, and using 3.4 g. of sodium, 14.3 g. of guanidine hydrochloride, and 34.3 g. of 3-(n-octylthio)propyl isocyanate, there was obtained 22.0 g. of 1-amidino-3= [3-(n-octylthio)propyl]urea having the structural formula as a white crystalline solid which melted at 84-85" C. The solubility of this base in a dilute acidic solution (0.35 ml. of N/2 hydrochloric acid plus 19.65 ml. of water) at 25 C. was less than 0.25 percent. In 95 percent ethyl alcohol at 25 C., it was soluble to the extent of 5 percent (w./v.); a precipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

EXAMPLE 37 Proceeding in a manner similar to that described in Example 1, and using 2.3 g. of sodium, 9.5 g. of guanidiue hydrochloride, and 22.9 g. of 3-(n-nonylthio)propy1 isocyauate, there was obtained 19.7 g. of 1-amidino-3-[3-(n-= nonylthio)propyl]urea, having the structural formula as a white crystalline solid which melted at 86-88 C. The solubility of this base in a dilute acidic solution (0.34 ml. of N/2 hydrochloric acid plus 19.66 ml. of water) at 25 C. was less than 0.25 percent. In 95 percent ethyl alcohol at 25 C., it was soluble to the extent of 5 percent (w./v.); a precipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

EXAMPLE 38 Proceeding in a manner similar to that described above in Example 1, and using 2.3 g. of sodium, 9.5 g. of guani dine hydrochloride. and 27.1 g. of 3 (n undecylthio)pro pyl isocyanate, there was obtained 16.6 g. of l-arnidince 3-[3-(nundecy1thio)propyllurea, having the structural formula N H O HaN JB NH NH O HQQ H Ha S GH Cl HQO O Ha as a white crystalline solid which melted at 91-93 (3. The solubility of this base in a dilute acidic solution (0.30 ml. of N/2 hydrochloric acid plus 19.70 ml. of water) at 25 C. was less than 0.25 percent. In 95 percent ethyl alcohol at 25 C., it was soluble to the extent of 5 percent (w./v.); a precipitate formed when the 5 percent alcoholic solution was diluted in four volumes of water.

EXAMPLE 39' Proceeding in a manner similar to that described above in Example 1, and using.2.3 g. of sodium, 9.5 g. of guanidine hydrochloride, and 28.5 g. of 3-(n-dodecylthio)pro-= pyl isocyanate, there was obtained 28.5 g. of 1-amidino- 3[3-(n-dodecylthio)propyl]urea, having the structural formula as a white crystalline solid which melted at 91-92 C. The solubility of this base in a dilute acidic solution (0.30 ml. of 'N/2 hydrochloric acid plus 19.70 ml. of water) at 25 C. was less than 0.25 percent. In 95 percent ethyl alcohol at 25 C., it was soluble to the extent of percent (w./v.); a precipitate formed when the 5 percent alcoholic solution was diluted with four volumes of water.

EXAMPLE 40 Proceeding in a manner similar to that described above in part (A) of Example 25, and using 1.96 g. of sodium, 12.5 g. of (3-morpholinopropyl)guanidine sulfate, and 7.2 g. of n-nonyl isocyanate, there was obtained 1-[(3- morpholinopropyl)amidino]-3-n-nonylurea having the structural formula and the dihydrochloride thereof. The dihydrochloride was obtained as a white powder which melted at 139-141" C. This salt was soluble in water at 25 C. to the extent of 20 percent; the pH of the 1 percent aqueous solution was 3.5, and when the pH was gradually raised by addition of N/ sodium hydroxide solution, no precipitate formed at pH 7.

EXAMPLE 41 Proceeding in a manner similar to that described above in part (A) of Example 25, and using 1.96 g. of sodium, 12.5 g. of (3- morpholinopropyl)guanidine sulfate, and 8.4 g. n-undecylisocyanate; there was obtained 1[(3-morpholinopropyl)amidino] -3-n-undecylurea having the structural formula EXAMPLE 42 Proceeding in a manner similar to that described above in part (A) of Example 25, and using 1.96 g. of sodium, 12.5 g. of (3-morpholinopropyl)guanidine sulfate, and 8.95 g. of n-dodecylisocyanate, there was obtained 1-[(3- morpholinopropyl)amidino1-3-n-dodecylurea having the structural formula and the dihydrochloride thereof. The dihydrochloride was obtained as a white powder which weighed 5.9 g. and which melted at 132-135 C. This salt was soluble in water at 25 C. to the extent of percent; the pH of the 1 percent aqueous solution was 3.8, and when the pH was gradually raised by addition of N/ 10 sodium hydroxide solution, no precipitate formed at pH 7.6.

24 Proceeding in accordance with the procedures described hereinabove and using the appropriate reactants, there are obtained the following further illustrative species of the compounds of Formulas I, II and III of the instant invention:

(1) 1-n-hexylamidino-3-(3,3-dimethylallyl)urea (2) 1- (4-dimethylaminobutylamidino)-3-cyclopropylurea (3) 1-(9-deceny1amidino) -3-(9-decenyl)urea (4) l-cyclohexylamidino-3-cyclopentylurea (5) l-cycloheptylaniidino 3- [4-(n-amyloxy)butyl] urea (6) l-(3-rnorpholinopropylarnidino)-3-(3-octenyl) thiourea (7) 1-(3-piperidinopropylamidino) -3- (3 -piperidino= propyl)thiourea (8) 1-n-hexylamidino-3-n-hexylthiourea (9) 1-n-heptylamidino-3-n-heptylthiourea (10) l-tert-octylarnidino-3-(3-morpholinopropyl)urea (11 1- 3- (n-octyloxy) propylamidino]-3-(3-morpho-= linopropyl)urea (12) l- (cyclobutylamidino) -3-[3-(n-decyloxy) propyl] thiourea (13) 1- (8-dimethylaminooctylamidino) -3-[3-(n-decylthio) propyl]-thiourea (l4) 1-n-octylamidino-3-'(3-propoxypropyl)urea (l5) l-iso-heptylamidino-S- [4-(propylthio)butyl]urea (16) 1-n-heptylamidino-3-(2-diisopropylaminoethyl) thiourea (17) l-cyclopentylamidino-3-n-undecylurea (18) l-cyclopropylamidino-B-(3-piperidinobutyl)urea (19) 1-(3-morpholinopropylamidino)-3-(4-morpholinobutyl urea (20) 1(Z-diethylaminoethylamidino)-3-(2-diethylaminoethyl)-thiourea '(21) 1-(2-dimethylaminopropylamidino)-3-(3-morpholinopropyl -thiourea (22) 1- 3- (n-decylthio) propylamidino] -3- 3-(n-decylthio) -propyl]urea (23) 1- [3- n-decylthio propylamidino -3-cyclohexylurea (24) 1-[4-(n-nonylthio)butylamidino]-3(5-morpholinoamyl)urea (25) 1-[3- (n-octyloxy)propylamidino] -3- 3- (n-octyb oxy)propyl] -urea (26) 1-[3-(n-heptyloxy)propylamidino]-3-(10-undecenyl urea (27) 1-cyclopentylamidino-3-(3,3-dimethylallyl)urea (28) 1- B-hexenyUamidinoJ-B- [3- (n-dodecylthio) propyl urea (29) 1-(3-di-n-butylaminopropylamidino)-3-(4= octenyl)urea 30) 1-methallylamidino-3-( 3-piperidinopropyl)urea (31) 1' (2-piperidinoethylamidino)3-(3 diethylamino prO yD-thiourea (32) 1-(3-piperidinopropylamidino)"3-[4-(n-propyl oxy) butyl] urea g2; 1-methylamidino-3- (2-ethylhexyl)urea Following are representative results obtained when the compounds prepared in accordance with the instant invention were tested in vitro by standard serial dilution procedures for bacteriostatic (Bs), bactericidal (Be), fungistatic (Fs), and fungicidal (Fe) properties; these results are expressed as minimum concentration of the test compound, in parts per million, required for no growth of the test organism. For example, in antibacterial tests, using Staphylococcus aureus 209, Salmonella typhosa Hopkins, Clvstridium welchl'i M, and Premiu 1-ethylamidino 3-isohexy1thiourea l n-heptylamidino-3-rnethylurea 1 (n-tetracosanylamidino)urea .1-amidino-3n-tetracosanylurea 1ndocosanylamidinQ-S methyIthiourea 1-[ (2-ethylhexyl)amidino]urea 1-amidino-2-(2-ethylhcxyl)urea monas aeruginosa 211, the results obtained were as fol lows:

infestans (late blight). And when this same compound at one-quarter pound per 100 gallons of water was Staph.aureus Sal. typhosa Cl. welchii Pa. aemg. Compound of Example No. Be Be Be Be Be Be Be Be 25 25 10 25 10 25 25 25 5 7. 5 5 5 7. 5 7. 5 7. 5 7. 5 2. 5 10 2. 5 10 2. 5 2. 5 5 10 5 10 25 25 2. 5 2. 5 75 100 2. 5 2. 5 5 6 2.5 2. 5 250 1000 2. 5 75 5 75 50 50 100 100 25 25 25 75 2. 5 2. 5 250 250 5 100 50 100 5 7. 5 750 1, 000 10 50 750 1,000 5 5 500 1,000 500 1,000 1,000 1, 000 25 25 1,000 1,000 7. 5 7. 5 7. 5 7. 5 7. 5 7. 5 7. 5 25 50 50 10 25 10 25 50 50 5 7. 5 5 7.5 5 5 25 25 7. 5 25 7. 5 l 5 50 75 50 10 25 10 10 50 50 7. 5 75 7. 5 10 5 5 50 75 7. 5 25 10 50 5 5 75 100 250 250 250 500 25 250 500 500 25 50 25 50 7. 5 25 250 250 50 50 25 50 5 25 250 250 25 25 25 25 2. 5 2. 5 100 100 5 5 7. 5 10 2. 5 5 50 75 10 20 5 7. 5 1 150 1 200 100 100 10 100 7. 5 1 150 1 200 100 100 15 15 7.5 10 1 100 1 200 100 150 10 15 7.5 10 1 100 1 200 100 150 10 7. 5 15 1 150 1 200 100 100 5 5 5 5 295 2. 5 50 100 24 5 25 5 7. 5 2. 5 2.5 50 75 25 -2H0l) 50 75 50 50 10 10 100 26 -2HC1) 7. 5 25 10 25 2. 5 2. 5 10 27 7. 5 50 7. 5 10 5 1 Proteus vulgarta ATOC 9920 was used instead of Cl. wclchti. I Escherichia colt was used instead of Sci. tz phosa.

C d fitmentaa. Aaniger Momalb.

ompoun o 1 Example No. Fe Fe Fe Fe Fe Fe 1A........... W... 100 100 10 10 1, 000 1, 000 100 1, 000 10 10 1,000 1, 000 100 1,000 .10 100 100 100 100 100 100 100 1,000 1,000 1,000 1,000 100 100 100 100 100 100 100 100 100 100 100 100 100 100 100 100 100 100 14 100 100 100 100 100 15 -HNOs)......... 10 10 100 100 0 100 10 100 100 .100 10 100 1, 000 1, 000 1,000 1, 000 1,000 100 100 100 100 100 100 100 100 100 100 100 100 .100 100 100 100 100 100 10 10 00 100 10 1.00 100 100 1, 0 1,000 1,000 1,000 100 100 100 100 100 100 Mufififflfl... 10g 100 lglig 100 Wm"... 1 1 I. :QeBu-JPBR a 100 so 30........... 75 100 100 25 mm... 50 mm... 25 mm... 75 100 50 50 100 1 i8 158 40 41% g 7.5 75 42 =2H0l 12.5 50

similarly applied to pinto beans, 86 percent protection was aiiorded against infection by Urflmyces phaseali typica (bean rust).

l amidinod-n-dodecylthiourea was found to aflord good protection against bacterial spot in tomato plants.

In commercial paper pulp having a native population of approximately one million organisms per gram, all organisms in the pulp were killed within one hour by 10 parts per million of l-amidino-3-n-undecylurea hydro= bromide, thus indicating the usefulness of this compound as a slime control agent in paper making.

We claim:

1. A process for combatting slime in paper pulp which comprises applying to said paper pulp an amount elicotive for combatting said slime of a compound selected from the group consisting of:

(a) a compound having the structural formula an x n nn ii nn g nn n' and (b) a compound having the structural formula NH X Y-NH-ii-NH-0--NH-T wherein: X in each instance is a member selected from the group consisting of oxygen and sulfur; one of R and R is alkyl. and the other of R and R is a member selected from the group consisting of hy-= drogen and alkyl, the total number of carbon atoms in R and R being 8-24; one of Y and Y is a member selected from the group consisting of hydrogen, alkyl containing 1-18 carbon atoms, alkenyl containing 3-18 carbon atoms, alkoxyalkyl containing 3-17 carbon atoms, alkylthioalkyl containing 3-17 carbon atoms, cycloalkyl containing 3-8 carbon atoms,

27 di(lower alkyl) aminoalkyl containing 4-10 carbon atoms, N-morpholinoalkyl containing 6-10 carbon atoms, and N-piperidinoalkyl containing 711 carbon atoms; and the other of Y and Y is a member of the group consisting of alkenyl containing 3-18 carbon atoms, alkoxyalkyl containing 317 carbon atoms, alkylthioal'kyl containing 3-17 carbon atoms, cycloalkyl containing 3-8 carbon atoms, di(lower alkyl) aminoalkyl containing 4-10 carbon atoms, N-morpholinoalkyl containing '6-10 carbon atoms, and N- piperidinoalkyl containing 7-11 carbon atoms. 2. A process according to claim 1 wherein the compound has the structural formula NH X HQN- -NH- -NH-R in which X is a member selected from the group consisting of oxygen and sulfur and R is alkyl containing 8-24 carbon atoms.

3. A process according to claim 1 wherein the compound has the structural formula a R-NH-i:-NH-i3NH:

in which X is a member selected from the group consisting of oxygen and sulfur and R is alkyl contiuing 8-24 carbon atoms.

4. A process according to claim 1 wherein the compound has the structural formula in which X is a member selected from the group consisting of oxygen and sulfur, and each of R and R is alkyl, the total number of carbon atoms in R and R being 8-24.

5. A process according to claim 1 wherein the compound has the structural formula NH X HzN- --NH- -NH-Y in which X is a member selected from the group consisting of oxygen and sulfur and Y' is alkenyl containing 3-18 carbon atoms.

6. A process according to claim 1 wherein the compound has the structural formula 28 in which X is a member selected from the group consisting of oxygen and sulfur, and Y is alkenyl containing 3-18 carbon atoms.

7. A process according to claim 1 wherein the compound has the structural formula in which X is a member selected from the group consisting of oxygen and sulfur and each of Y and Y is alkenyl containing 3-18 carbon atoms.

8. A process according to claim 2 wherein the compound is 1-amidino-3-decylurea.

9. A process according to claim 2 wherein the com= pound is 1-amidino-3-undecylurea.

10. A process according to claim 2 wherein the compound is 1-amidino-3-dodecylurea.

11. A process according to claim 4 wherein the compound is 1-hexylamidino-3-hexylurea.

12. A process according to claim 4 wherein the compound is 1-heptylamidino-3-hexylurea.

13. A process according to claim 4 wherein the com pound is 1-heptylamidino-3-heptylurea.

14. A process according to claim 4 wherein the compound is 1-octylamidino-3-octylurea.

References Cited UNITED STATES PATENTS 2,631,152 3/1953 Ritter et a1. 260--239.1 3,364,140 1/1968 Wehner 161-161 X OTHER REFERENCES Slotta et al.: Berichte, vol. 63 (1930), pp. 212-16.

Junod: Helvetica Chimica Acta., vol. (1952), p. 1670.

Dotta et al.: J. Indian Chem. Soc., vol. (1963), pp. 863-64.

S. LEON BASHORE, Primary Examiner F. FREI, Assistant Examiner US. Cl. XR. 106-45 AF 